Назив: | Dielectric studies of barium bismuth titanate as a material for application in temperature sensors | Аутори: | Cvejin, Katarina Mojić, Bojana Samardžić, Nataša Srdić, Vladimir Stojanović, Goran |
Датум издавања: | 2013 | Издавач: | Springer Link | Часопис: | Journal of Materials Science: Materials in Electronics | Сажетак: | Ceramic nanocrystalline samples with composition Ba1-3aBi 2aTiO3 were synthesized by sol-gel method, for different values of parameter a (for a = 0.0165, 0.033, 0.050). In order to determine whether barium bismuth titanate is suitable for application in temperature sensors, dielectric properties measurements were conducted on the prepared samples, as a function of both temperature (from room temperature up to 190 C) and frequency (from 50 kHz to 1 MHz). Real and imaginary parts of dielectric constant were determined using an Impedance Analyzer HP-4194A. Depending on parameter a two different behavior were determined: (1) classical ferroelectric behavior, for the sample with low a value and (2) relaxor behavior for the samples with higher a values. Thus, a typical characteristic of relaxor ferroelectrics with a broad and dispersive dielectric maximum was observed for the samples Ba0.85Bi0.1TiO3 and Ba 0.90Bi0.066TiO3. Temperature dependence (for real part of dielectric constant εr′) is almost linear, for lower temperatures than peak value (slope +1.3 1/ C), and higher than this value (slope -1 1/ C). The feature of linearity is very important from practical aspects of application of this material in wireless temperature sensors. The temperature coefficient of dielectric constant for the sample with the best linearity (Ba0.95Bi0.033TiO3 at 1 MHz) was found to vary from positive one +3.72 × 10-3 1/ C to negative value -2.85 × 10-3 1/ C, in the temperature range 25-190 C. © 2012 Springer Science+Business Media New York. | URI: | https://open.uns.ac.rs/handle/123456789/9030 | ISSN: | 9574522 | DOI: | 10.1007/s10854-012-0914-3 |
Налази се у колекцијама: | FTN Publikacije/Publications TF Publikacije/Publications |
Приказати целокупан запис ставки
SCOPUSTM
Навођења
7
проверено 03.05.2024.
Преглед/и станица
35
Протекла недеља
7
7
Протекли месец
4
4
проверено 10.05.2024.
Google ScholarTM
Проверите
Алт метрика
Ставке на DSpace-у су заштићене ауторским правима, са свим правима задржаним, осим ако није другачије назначено.