Назив: | Effect of austempering temperature on cavitation behaviour of unalloyed ADI material | Аутори: | Dojcinovic M. Eric O. Rajnović, Dragan Sidjanin L. Baloš, Sebastian |
Датум издавања: | 17-јун-2013 | Часопис: | Materials Characterization | Сажетак: | This paper provides an in-depth study and description of cavitation damage and microstructural changes in two types of unalloyed austempered ductile iron (ADI). ADI materials used were austempered at 300 and 400 C having ausferrite microstructure with 16 and 31.4% of retained austenite, respectively. Metallographic examination was carried out to study the morphology of their cavitation-damaged surfaces. Cavitation damage was initiated at graphite nodules as well as in the interface between a graphite nodule and an ausferrite matrix. Furthermore, microcracking and ferrite/retained austenite morphology were proved to be of great importance for cavitation resistance. Mass loss rate revealed that ADI austempered at 400 C has a higher cavitation resistance in water than ADI austempered at 300 C. A higher amount of retained austenite in ADI austempered at 400 C played an important role in increasing cavitation resistance. The good cavitation behaviour of ADI austempered at 400 C was due to the matrix hardening by stress assisted phase transformation of retained austenite into martensite (SATRAM) phenomenon, as shown by X-ray diffraction analysis. © 2013 Published by Elsevier Inc. | URI: | https://open.uns.ac.rs/handle/123456789/8858 | ISSN: | 10445803 | DOI: | 10.1016/j.matchar.2013.05.005 |
Налази се у колекцијама: | FTN Publikacije/Publications |
Приказати целокупан запис ставки
SCOPUSTM
Навођења
25
проверено 10.05.2024.
Преглед/и станица
30
Протекла недеља
9
9
Протекли месец
0
0
проверено 10.05.2024.
Google ScholarTM
Проверите
Алт метрика
Ставке на DSpace-у су заштићене ауторским правима, са свим правима задржаним, осим ако није другачије назначено.