Nаziv: | Abrasive wear behaviour of ADI material with various retained austenite content | Аutоri: | Baloš, Sebastian Rajnović, Dragan Dramićanin, Miroslav Labus D. Eric-Cekic O. Grbovic-Novakovic J. Sidjanin L. |
Dаtum izdаvаnjа: | 3-јул-2016 | Čаsоpis: | International Journal of Cast Metals Research | Sažetak: | © 2016 Informa UK Limited, trading as Taylor & Francis Group. In this paper, the wear rate of ferritic and pearlitic ductile iron, as well as three types of austempered ductile iron (ADI materials), austempered at 300, 350 and 400 °C is investigated. Two wear parameters were varied, wear load (0.5, 1.3, 2 kg) and grit paper abrasive grain size (P240, P500, P800). The hardness of ductile iron and stress-assisted phase transformation of retained austenite into martensite (SATRAM) phenomenon in ADI materials were found to play major roles in wear behaviour. The pronounced SATRAM phenomenon was detected for the most severe wear parameters. Another important factor in the occurrence of SATRAM phenomenon is the presence of metastable, low carbon-enriched retained austenite. As a consequence, the wear rate of ADI austempered at 400 °C is nearly equivalent to ADI austempered at 300 °C at medium and high loading with the coarsest abrasive paper grit tested (P240). | URI: | https://open.uns.ac.rs/handle/123456789/4607 | ISSN: | 13640461 | DOI: | 10.1080/13640461.2015.1125982 |
Nаlаzi sе u kоlеkciјаmа: | FTN Publikacije/Publications |
Prikаzаti cеlоkupаn zаpis stаvki
SCOPUSTM
Nаvоđеnjа
15
prоvеrеnо 06.05.2023.
Prеglеd/i stаnicа
30
Prоtеklа nеdеljа
2
2
Prоtеkli mеsеc
4
4
prоvеrеnо 10.05.2024.
Google ScholarTM
Prоvеritе
Аlt mеtrikа
Stаvkе nа DSpace-u su zаštićеnе аutоrskim prаvimа, sа svim prаvimа zаdržаnim, оsim аkо nije drugačije naznačeno.