Nаziv: | Notch fracture toughness of high-strength Al alloys | Аutоri: | Vratnica M. Pluvinage G. Jodin P. Cvijović Z. Rakin M. Burzić, Z. Gerić, K. |
Dаtum izdаvаnjа: | 1-јан-2013 | Čаsоpis: | Materials and Design | Sažetak: | In this study, the notch fracture toughness (nft) of high-strength Al alloys was examined by a non-standardized procedure. the nft is defined as the critical notch stress-intensity factor (nsif) kρ,c, which is determined by using several methods of analysis and computing. a set of specimens with different notch root radii made from overaged 7xxx alloy forging was selected. the influence of the notch radius on the fracture toughness of the material was considered. it was found that the notch radius strongly affects the fracture behavior of forged 7xxx alloy in overaged condition. the notch fracture toughness was higher than the fracture toughness of a cracked specimen and increased linearly with notch radius. the critical notch radius was related to the spacing of intermetallic (im) particles which promote an intergranular or transgranular fracture mechanism according to their size. it appeared that ductile transgranular fracture generated by the formation of dimples around dispersoids and matrix precipitates was predominant which indicates that intense strains are limited to a much smaller zone than the coarse im particles spacing. this double mechanism is also operate for crack propagation of ductile fatigue. the nature and morphology of im particles exert significant effects on the rate of fatigue crack growth and fracture toughness properties. © 2012 Elsevier Ltd. | URI: | https://open.uns.ac.rs/handle/123456789/11867 | ISSN: | 02613069 | DOI: | 10.1016/j.matdes.2012.07.031 |
Nаlаzi sе u kоlеkciјаmа: | Naučne i umetničke publikacije |
Prikаzаti cеlоkupаn zаpis stаvki
SCOPUSTM
Nаvоđеnjа
20
prоvеrеnо 12.08.2023.
Prеglеd/i stаnicа
12
Prоtеklа nеdеljа
10
10
Prоtеkli mеsеc
0
0
prоvеrеnо 03.05.2024.
Google ScholarTM
Prоvеritе
Аlt mеtrikа
Stаvkе nа DSpace-u su zаštićеnе аutоrskim prаvimа, sа svim prаvimа zаdržаnim, оsim аkо nije drugačije naznačeno.