Tribological behavior of duplex coating improved by ion implantation

Abstract

In the present paper the tribological behavior of the coatings are discussed. Duplex coatings were applied on cold working steel 100Cr6. Samples were plasma nitrided at different thickness of plasma surface layers. TiN was deposited with a classic BALZERS PVD equipment and subsequent ion implantation. Ion implantation was provided with N5+ ions. The other samples were produced with IBAD technology in DANFYSIK chamber. Wear resistance and exchanges of friction coefficient were measured with on-line test using special designed tribology equipment. Following the tests, the wear zone morphology and characteristics of surface layer structure as well as important properties were investigated by scanning electron microscopy (SEM) and X-ray diffraction analysis (XRD). Scratch adhesion testing was performed using commercially available equipment. Energy dispersive X-ray analysis (EDAX) of the wear-scars on pins provided essential information on the wear characteristics. In this paper some results related to influence of duplex coating production methodology on tribological behavior for cold working steel was presented. © 2003 Elsevier B.V. All rights reserved.