Nаziv: | Mechanical characteristics of As<inf>2</inf>S<inf>3</inf> glasses induced by doping with bismuth | Аutоri: | Šiljegović, Mirjana Lukić-Petrović, Svetlana Petrović, Đorđe Videnović I. Turyanytsa I. |
Dаtum izdаvаnjа: | 1-апр-2016 | Čаsоpis: | Acta Physica Polonica A | Sažetak: | This paper presents and discusses the results of the instrumented indentation test of the samples of the system Bix(As2S3)100-x, x = 1:5, 3, 5, and 7 at.%. Measurements of mechanical parameters were performed using a Fischerscope HM2000 S nanoindentation device. The experimental data obtained by measuring the microhardness parameters were used to determine some other mechanical quantities that are important for the characterization of the examined materials in terms of their potential applications. For the first three compositions, the results indicated an increase in the microhardness with the increase in the content of doping atoms, which can be interpreted as an enhancement of the strength and stiffness of the structural network. The lower value of microhardness of the sample with the maximum content of Bi can BE associated with the specific structure of this composition. The pronounced indentation size effect was also detected on the indentation curve in the range of smaller loads. According to the model of elastic-plastic deformation, applied for the description of indentation size effect measured for the investigated chalcogenides, the largest value of the elastic recovery was observed for the sample Bi7(As2S3)93. The calculated values of the elasticity modulus show that the glass with x = 5 at.% Bi is characterized with the highest atomic packing density. | URI: | https://open.uns.ac.rs/handle/123456789/4776 | ISSN: | 05874246 | DOI: | 10.12693/APhysPolA.129.488 |
Nаlаzi sе u kоlеkciјаmа: | PMF Publikacije/Publications |
Prikаzаti cеlоkupаn zаpis stаvki
SCOPUSTM
Nаvоđеnjа
4
prоvеrеnо 03.05.2024.
Prеglеd/i stаnicа
22
Prоtеklа nеdеljа
9
9
Prоtеkli mеsеc
0
0
prоvеrеnо 10.05.2024.
Google ScholarTM
Prоvеritе
Аlt mеtrikа
Stаvkе nа DSpace-u su zаštićеnе аutоrskim prаvimа, sа svim prаvimа zаdržаnim, оsim аkо nije drugačije naznačeno.