Назив: | Alumina doped zirconia nanopowders: Wet-chemical synthesis and structural analysis by Rietveld refinement | Аутори: | Srdić, Vladimir Rakić, Srđan Cvejić, Željka |
Датум издавања: | 2-окт-2008 | Издавач: | Elsevier | Часопис: | Materials Research Bulletin | Сажетак: | Alumina/zirconia nanopowders, with up to 20 mol% Al2O3, were prepared by wet-chemical synthesis technique, using controlled hydrolysis of alkoxides. The as-synthesized powders are amorphous, have very high specific surface area and the corresponding particle size smaller than 4 nm. Amorphous powders with 0, 10 and 20 mol% Al2O3 crystallize at 460, 692 and 749 °C, respectively, as a single-phase tetragonal zirconia, without any traces of alumina phases. Rietvled refinement of X-ray diffraction data, used for the detailed structural analysis of annealed nanopowders, showed that the high-temperature zirconia phase is stabilized due to the formation of ZrO2/Al2O3 solid solutions. High solubility of alumina in the tetragonal zirconia (up to 28.6 at% Al3+) and stabilization of tetragonal zirconia solid solution up to high temperature (as high as 1150 °C) were also confirmed. | URI: | https://open.uns.ac.rs/handle/123456789/24647 | ISSN: | 00255408 | DOI: | (BISIS)25537 |
Налази се у колекцијама: | PMF Publikacije/Publications TF Publikacije/Publications |
Приказати целокупан запис ставки
Преглед/и станица
39
Протекла недеља
10
10
Протекли месец
0
0
проверено 10.05.2024.
Google ScholarTM
Проверите
Алт метрика
Ставке на DSpace-у су заштићене ауторским правима, са свим правима задржаним, осим ако није другачије назначено.