Nаziv: | Lithium and lead chloride antimonate glasses | Аutоri: | Castro Alexandre Bréhault Antoine Carcreff Julie Bošak Ondrej Kubliha Marian Trnovcová Viera Dománková Mária Šiljegović Mirjana Calvez Laurent Labaš Vladimir |
Dаtum izdаvаnjа: | 2018 | Čаsоpis: | Journal of Non-Crystalline Solids | Sažetak: | © 2018 Elsevier B.V. The glass-forming domain in the new Sb2O3-PbCl2-LiCl system has been delimited. Systematic investigations were undertaken to establish the influence of each starting component on the characteristic temperatures (Tg and Tx) and the density. Glasses have Tg between approximately 255 °C and 310 °C for the richest LiCl and the free LiCl compositions, respectively. A decrease of the network connectivity due to the PbCl2 or LiCl is supported by the data. AC, DC, and Thermally Simulated Deposition Current (TSDC) measurements were carried out to study the electrical properties of the lithium and lead chloride antimonate glasses. The interpretation of the results was supplemented by X-ray diffraction and TEM measurements in order to identify and quantify the crystalline phases observed in crystallized compositions after quenching. The positive effect of PbCl2 on conductivity was established although the TSDC demonstrates the Li+ ions can be considered as the only charge carriers in this system. | URI: | https://open.uns.ac.rs/handle/123456789/19560 | ISSN: | 0022-3093 | DOI: | 10.1016/j.jnoncrysol.2018.07.015 |
Nаlаzi sе u kоlеkciјаmа: | PMF Publikacije/Publications |
Prikаzаti cеlоkupаn zаpis stаvki
SCOPUSTM
Nаvоđеnjа
2
prоvеrеnо 10.05.2024.
Prеglеd/i stаnicа
20
Prоtеklа nеdеljа
10
10
Prоtеkli mеsеc
0
0
prоvеrеnо 10.05.2024.
Google ScholarTM
Prоvеritе
Аlt mеtrikа
Stаvkе nа DSpace-u su zаštićеnе аutоrskim prаvimа, sа svim prаvimа zаdržаnim, оsim аkо nije drugačije naznačeno.