Назив: | Electrical conductivity of sol-gel derived yttria-stabilized zirconia | Аутори: | Srdić, Vladimir Omorjan, Radovan |
Датум издавања: | 2001 | Издавач: | Elsevier | Часопис: | Ceramics International | Сажетак: | A 3 mol% Y2O3 zirconia stabilized powder has been synthesized by destabilization of an aqueous zirconia sol prepared by the alkoxide hydrolysis method. The powder calcined at 500°C is ultrafine with tetragonal crystallites of about 8 nm, slightly agglomerated and with a narrow pore size distribution having an average pore size of 5.2 nm. Zirconia ceramics with density higher than 92%TD and grain size on the order of 100 nm have been obtained by uniaxial pressing at 500 MPa and vacuum sintering at 1000°C. Electrical conductivity of sintered samples, evaluated by complex impedance spectroscopy measurements, indicated that the zirconia stabilized with 3 mol% Y2O3 can potentially be used as an oxygen semipermeable dense membrane, but only at a relatively high temperature. © 2001 Elsevier Science Ltd and Techna S.r.l. All rights reserved. | URI: | https://open.uns.ac.rs/handle/123456789/15789 | ISSN: | 02728842 | DOI: | 10.1016/S0272-8842(01)00041-4 |
Налази се у колекцијама: | TF Publikacije/Publications |
Приказати целокупан запис ставки
SCOPUSTM
Навођења
22
проверено 03.05.2024.
Преглед/и станица
33
Протекла недеља
12
12
Протекли месец
1
1
проверено 10.05.2024.
Google ScholarTM
Проверите
Алт метрика
Ставке на DSpace-у су заштићене ауторским правима, са свим правима задржаним, осим ако није другачије назначено.