Nаziv: | Benefits of mesopores in nanocristalline Pd/SnO<inf>2</inf> catalysts for nitrate hydrogenation | Аutоri: | Kovačević M. Kiš E. Bošković G. |
Dаtum izdаvаnjа: | 1-дец-2007 | Čаsоpis: | Acta Periodica Technologica | Sažetak: | Mesoporous nanocristalline SnO2 supports were synthesized by a modified sol-gel method starting from SnCl2-2H2O and citric acid at pH 2.0 and 9.5. Noble metal was introduced via wet impregnation using PdCl2 as active phase precursor. Catalysts activities in water denitration were correlated with their textural, structural and morphological properties using LTNA (BET), XRD and SEM /EDS analysis. Lower pH value during the catalyst synthesis resulted in a final material characterized with more developed porosity and higher surface area. Although both catal ' ysts turned out to be tailored from nanoscale crystallites, higher pore fraction of mesopores resulting from the thesis in acidic conditions, was found to be responsible for superior catalytic behaviour. | URI: | https://open.uns.ac.rs/handle/123456789/15030 | ISSN: | 14507188 | DOI: | 10.2298/APT0738O69K |
Nаlаzi sе u kоlеkciјаmа: | TF Publikacije/Publications |
Prikаzаti cеlоkupаn zаpis stаvki
SCOPUSTM
Nаvоđеnjа
2
prоvеrеnо 03.05.2024.
Prеglеd/i stаnicа
11
Prоtеklа nеdеljа
6
6
Prоtеkli mеsеc
0
0
prоvеrеnо 10.05.2024.
Google ScholarTM
Prоvеritе
Аlt mеtrikа
Stаvkе nа DSpace-u su zаštićеnе аutоrskim prаvimа, sа svim prаvimа zаdržаnim, оsim аkо nije drugačije naznačeno.