Назив: | Humidity sensing properties of nanocrystalline pseudobrookite (Fe <inf>2</inf> TiO <inf>5</inf> ) based thick films | Аутори: | Nikolić, Milica Vasiljevic Z. Lukovic M. Pavlović, Vladimir Vujancevic J. Radovanović, Milan Krstic J. Vlahović, Branislav Pavlović, Vladimir |
Датум издавања: | 20-дец-2018 | Часопис: | Sensors and Actuators, B: Chemical | Сажетак: | © 2018 Elsevier B.V. Pseudobrookite based nanopowder was obtained by solid state synthesis of starting hematite and anatase nanopowders in the weight ratio 55:45. Structural and morphological properties were analyzed using X-ray diffraction (XRD), BET, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, UV/Vis diffuse reflectance spectroscopy, Field emission scanning electron microscopy (FESEM) and Transmission electron microscopy (TEM) confirming the formation of nanocrystalline pseudobrookite. The obtained powder was mixed with a binder (ethyl cellulose), dispersant (α-terpinol) and adhesion agents (acetic acid and distilled water) to obtain a thick film paste. It was screen printed on alumina substrate with interdigitated PdAg electrodes and fired at 600 °C for 30 min. Formation of a porous nanocrystalline thick film structure was shown using Scanning electron microscopy (SEM), while Hall measurements enabled determination of carrier mobility. Change of impedance response in the frequency range 42 Hz–1 MHz with humidity was analyzed at room temperature (25 °C) and 50 °C in the relative humidity range 30–90% and 40–90%, respectively. At 42 Hz, and room temperature the impedance reduced ∼28 times, while at 50 °C it reduced ∼147 times in the relative humidity range 40–90%. The sensor showed rapid response (16 s) and relatively low hysteresis (8.39% at 25 °C and 2.64% at 50 °C) showing that this is a promising material for application in humidity sensing. | URI: | https://open.uns.ac.rs/handle/123456789/1026 | ISSN: | 09254005 | DOI: | 10.1016/j.snb.2018.09.063 |
Налази се у колекцијама: | POLJF Publikacije/Publications |
Приказати целокупан запис ставки
SCOPUSTM
Навођења
36
проверено 20.11.2023.
Преглед/и станица
35
Протекла недеља
5
5
Протекли месец
3
3
проверено 10.05.2024.
Google ScholarTM
Проверите
Алт метрика
Ставке на DSpace-у су заштићене ауторским правима, са свим правима задржаним, осим ако није другачије назначено.